Üçlü silindirler
Farklı hızlarda dönen üç silindirin arasına giren pigment topaklarını etkin biçimde ezerek disperse eden bir boya üretim aracı. Üçlü silindirler, çok etkin ezme özelliklerine rağmen, düşük üretim miktarları nedeniyle giderek daha az kullanılmaktadırlar.
Three roll mills
Paint production equipment, which disperses by efficiently grinding the pigment flocs passing through nips of three rollers revolving at different speeds. Although they perform effective dispersion, their use is much more limited today because of their capacity limitations.
Üçlü uyarıcı değerler
İnsan gözünün ağ tabakasındaki üç farklı türde hücre mavi, yeşil ve kırmızı renkteki ışıklara hassastır. Herhangi bir rengin bu renkleri ne miktarda içerdiği renk spektrofotometreleriyle ölçülür. Bulunan değerler, o rengin üçlü uyarıcı değerleridir. Üçlü uyarıcı değerler X, Y ve Z simgeleriyle ifade edilirler.
Tristimulus values
Three different receptor cells in the retina of human eye are sensitive to blue, green and red lights. Color spectrophotometers are utilized to measure how much a color comprises these lights. Results will be tristimulus values expressed in X, Y, Z symbols.
Üre
Hint yağı türevleri
Hint yağındaki OH grupları üzerinden boya bağlayıcılarıyla hidrojen bağları kurma yatkınlığında olan bu katkılar, boyaya tiksotropik bir yapı kazandırırlar. Boya üretimi sırasındaki yüksek sıcaklıklara hassas olmaları, zayıf yanlarını oluşturur.
Kuruma süresi
Yaş boyanın uygulanmasının ardından istenen kuruma düzeyine erişilme süresi kuruma süresi, kuruma zamanı olarak anılır. İstenen kuruma düzeyine bağlı olarak bir organik kaplama için toz kuruması süresi, dokunma kuruması süresi, montaj kuruması süresi, istif kuruması süresi ve kimyasal kuruma süresi gibi farklı kuruma sürelerinden söz edilebilir.
Nemle sertleşen poliüre kaplamalar
Bkz. Nemle sertleşen kaplamalar
Nemle sertleşen poliüretan kaplamalar
İzosiyanat fonksiyonlu reçinelerin nemle girdikleri tepkime sonucunda poliüre bileşikleri oluşmasına karşın, bu bağlayıcıları içeren kaplamalara, yaygın bir yanlış adlandırmayla “Nemle sertleşen poliüretan kaplamalar” denilmektedir.
Poliüretan reçineleri
Bkz. Üretan reçineleri
Tek pigmentli pastalarla boya üretimi
Bu boya üretim yaklaşımında, geniş bir bağlayıcı uyuşurluğuna sahip bir reçine, ortak dispersiyon reçinesi olarak seçilir ve bu reçine içinde, çeşitli pigmentler ayrı ayrı ezilerek istenen ezme inceliğine getirilir. Daha sonra, istenen bir boya rengi bu pastalar kullanılarak renk eşlemesi yapılır ve uygun hesaplamalarla miktarları belirlenen diğer girdilerle boyanın alt ilavesi yapılır. Bu yaklaşımın başlıca üstünlükleri, uyuşur reçine kullanarak çeşitli ürün grupları için kullanılabilen ortak pastalar yapıp değirmenler başta olmak üzere üretim aracı kapasitelerinin ve stok alanlarının daha iyi optimize edilmesi ve hızlı üretim yapılabilmesidir. Yaklaşımın öne çıkan zayıf yanlarıysa, derişik pigment pastaları kullanılması nedeniyle hassas renk eşlemenin yapılamaması; derişik pasta ortamındaki pigmentlerin, zaman içinde yumaklaşarak, renk şiddeti düşüklüğü, parlaklık kaybı, tanecik oluşumu, pusluluk gibi sorunlara yol açmaları olarak sayılabilir.
Üre
Sıvı CO2 ile amonyağın tepkimesi sonucu üretilen ve üre formaldehit reçinelerinin sentezinde kullanılan bileşik.
Erime noktası: 132-136°C
Üre formaldehit reçineleri
Üre ile formaldehitin polimerleşmesiyle sentezlenen reçinelerdir. Büyük ölçüde yapıştırıcı olarak kullanılırlar. Fırın kurumalı organik kaplamalarda da alkid ve polyester reçinelerinin çapraz bağlayıcısı olarak kullanılırlar.
Üretan modifiye reçineler
Temel yapısı itibariyle alkid, akrilik vd. olup, izosiyanat grupları içeren monomer ve prepolimerlerle modifiye edilerek esneklik, kimyasal direnç vd. özellikleri iyileştirilen reçineler.
Üretan reçineleri
Üretan reçineleri, molekülünde en az iki izosiyanat grubu bulunan bileşiklerin, molekülünde birden fazla hidroksil grubu bulunduran bileşiklerle verdikleri tepkimeler sonucunda oluşurlar. Yüksek su, çözgen ve kimyasal direncine sahip olan esnek kaplamalar verirler. Aromatik yapılar içermeyen üretan reçienleri, ayrıca çok yüksek ışık dayanımına sahip kaplamalar verirler.
Üretim kalitesi
Bir ürün ya da hizmetin üretilmesi sürecinin sonunda, tasarım aşamasında öngörülen niteliklere ne oranda sahip olduğunun ölçüsü. Ayrıca Bkz. Tasarım kalitesi
Urea
Castor oil derivatives
Castor oil derivatives, having tendencies to establish hydrogen bonds with the binders over their OH groups, provide the coating with a thixotropic structure. Sensitivity to high temperatures applied during paint production can be noted as their weakness.
Drying time
Time period required to reach the desired drying level after application, is defined as the drying time. Depending on the drying level, various drying times can be mentioned such as dust-free drying time, dry-to-touch time, dry-to-assembly time, dry-to-stack time and chemical drying time etc.
Moisture curing polyurea coatings
See Moisture curing coatings
Moisture curing polyurethane coatings
Despite the fact that, polyurea is formed from the reaction of isocyanate with moisture in the air, coatings composed of polyurea is commonly misnamed as “moisture curing polyurethane coatings”.
Polyurethane resins
See Urethane resins
Paint production using monopigmented pigment pastes
In this paint production approach, a resin with a high compatibility range is selected as main dispersion resin and different pigments are dispersed separately to a certain grain size using this resin. Color matching is performed using this pigment pastes and letdown is done by adding remaining ingredients after a proper calculation. The main advantages of this approach are, better optimization of capacity of production equipment (especially the mills) and storage areas in addition to reduced production times. It is achieved by producing common pigment pastes, which can be used in various product groups owing to the compatible resin used. The drawback of this approach is the difficulties in sensitive color matching because of highly concentrated pigment pastes in addition to the possibility of decrease in color strength, gloss as well as haze and formation of particles due to pigment flocculation during storage.
Urea
Compound produced by reaction of liquid CO2 with ammonia and used in the synthesis of urea formaldehyde resin.
Melting point: 132-136°C
Urea formaldehyde resins
Polymerization product of urea and formaldehyde. Commonly used as adhesives. In addition, they are used as cross-linker in alkyd and polyester baking systems.
Urethane modified resins
Resins that have alkyd, acrylic structures but modified with monomers and prepolymers containing isocyanate groups to improve flexibility, chemical resistance and so on.
Urethane resins
Urethane resins are formed by reactions of compounds bearing at least two isocyanate groups with molecules with more than one hydroxyl groups. Urethane coatings have high water, solvent and chemical resistance. Urethane coatings with no aromatic groups have superior UV resistance.
Production quality
Assessment of how close the characteristics of a product and service are after production process, relative to those projected during design stage. See Also Design quality
Üre formaldehit reçineleri
Üre ile formaldehitin polimerleşmesiyle sentezlenen reçinelerdir. Büyük ölçüde yapıştırıcı olarak kullanılırlar. Fırın kurumalı organik kaplamalarda da alkid ve polyester reçinelerinin çapraz bağlayıcısı olarak kullanılırlar.
Urea formaldehyde resins
Polymerization product of urea and formaldehyde. Commonly used as adhesives. In addition, they are used as cross-linker in alkyd and polyester baking systems.
Üretan modifiye reçineler
Temel yapısı itibariyle alkid, akrilik vd. olup, izosiyanat grupları içeren monomer ve prepolimerlerle modifiye edilerek esneklik, kimyasal direnç vd. özellikleri iyileştirilen reçineler.
Urethane modified resins
Resins that have alkyd, acrylic structures but modified with monomers and prepolymers containing isocyanate groups to improve flexibility, chemical resistance and so on.
Üretan reçineleri
Poliüretan reçineleri
Bkz. Üretan reçineleri
Üretan reçineleri
Üretan reçineleri, molekülünde en az iki izosiyanat grubu bulunan bileşiklerin, molekülünde birden fazla hidroksil grubu bulunduran bileşiklerle verdikleri tepkimeler sonucunda oluşurlar. Yüksek su, çözgen ve kimyasal direncine sahip olan esnek kaplamalar verirler. Aromatik yapılar içermeyen üretan reçienleri, ayrıca çok yüksek ışık dayanımına sahip kaplamalar verirler.
Urethane resins
Polyurethane resins
See Urethane resins
Urethane resins
Urethane resins are formed by reactions of compounds bearing at least two isocyanate groups with molecules with more than one hydroxyl groups. Urethane coatings have high water, solvent and chemical resistance. Urethane coatings with no aromatic groups have superior UV resistance.
Üretim kalitesi
Bir ürün ya da hizmetin üretilmesi sürecinin sonunda, tasarım aşamasında öngörülen niteliklere ne oranda sahip olduğunun ölçüsü. Ayrıca Bkz. Tasarım kalitesi
Tasarım kalitesi
Bir ürün ya da hizmetin tasarlanması sırasında, ürünün ya da hizmetin sahip olması öngörülen özellikler toplamının ortaya çıkardığı kalite. Örneğin, bir pizza şirketi, tipi ve içeriği tanımlanmış 10 çeşit pizza için internetten sipariş alıp, şehirdeki tüm adreslere 20 dakikada ve sıcak ve hijyenik ürün teslimatı yapmak biçimindeki bir hizmet tasarımıyla kurulabilir. (Bkz.Soyulabilir boyalar). Buna karşın başka bir pizzacı, sıcaklığı yaz-kış 25ºC olan ve masalarında vazo içinde taze çiçek bulunan salonunda, içeriğini müşterinin seçerek belirleyeceği pizzaları en geç 15 dakika içinde masaya servis etmek tasarımıyla kurulmuş olabilir. İki hizmet arasındaki fark, tasarım kaliteleri arasındaki farktan kaynaklanmaktadır.
Ayrıca Bkz. Üretim kalitesi
Soyulabilir boyalar
Uygulandığı yüzeye geçici bir süreyle koruyuculuk sağlaması hedeflenen, öngörülen geçici süre sona erdikten sonra kolayca soyularak yüzeyden ayrılan boyalar.
Production quality
Assessment of how close the characteristics of a product and service are after production process, relative to those projected during design stage. See Also Design quality
Design quality
Total quality arisen from the predicted qualifications of a product or a service during the design stage. For instance, a pizza shop could be founded to take orders of 10 different pizzas of which ingredients are predefined, via internet and deliver these orders to all locations in the city within 20 minutes in a hot and hygienic condition. (See Peelable coatings). On the other hand, another pizza shop, could be founded to serve pizzas in the shop in which its temperature is held constant in summer and winter at 25ºC and there are fresh flowers in a vase at each table. Customers choose the ingredients of pizza and they will be served at most 15 minutes. The difference between two services is stem from the difference between their design qualities.
See Also Production quality
Strip coats / Strippable coatings / Peelable coatings
Paints that can provide protection for a certain time to the surface on which they applied and after this period, they can be easily removed from the surface.